Anodic formation of self-organized Ti(Nb,Sn) oxide nanotube arrays with tuneable aspect ratio and size distribution
Fornell Beringues, Jordina (Universitat Autònoma de Barcelona. Departament de Física)
Oliveira, N. T. C. (Universidade Federal de São Carlos. Departamento de Engenharia de Materiais)
Pellicer Vilà, Eva Maria (Universitat Autònoma de Barcelona. Departament de Física)
Steenberge, Nele van (OnderzoeksCentrum voor de Aanwending van Staal)
Baró, M. D.. (Universitat Autònoma de Barcelona. Departament de Física)
Bolfarini, C. Claudemiro (Universidade Federal de São Carlos. Departamento de Engenharia de Materiais)
Sort Viñas, Jordi (Universitat Autònoma de Barcelona. Departament de Física)
Fecha: |
2013 |
Resumen: |
In the present communication one-step anodization is used to prepare large arrays of self-assembled Ti(Nb,Sn) oxide nanotubes on Ti-Nb-Sn alloy. Tuneable nanoscale geometries (unimodal vs. bimodal size distribution with variable length/diameter ratios) can be controllably achieved by varying the anodization conditions, which are highly desirable for enhanced functionalities in widespread applications. |
Ayudas: |
Ministerio de Economía y Competitividad MAT2011-27380-C02-01
|
Nota: |
This is the author's version of a work that was accepted for publication in Electrochemistry communications. Changes resulting from the publishing process, such as peer review, editing, corrections, structural formatting, and other quality control mechanisms may not be reflected in this document. Changes may have been made to this work since it was submitted for publication. A definitive version was subsequently published in Electrochemistry communications, [33,(2013)] DOI10.1016/j.elecom.2013.04.023). |
Derechos: |
Tots els drets reservats. |
Lengua: |
Anglès |
Documento: |
Article ; recerca ; Versió acceptada per publicar |
Materia: |
Titani ;
Materials -- Propietats elèctriques ;
Nanotubs |
Publicado en: |
Electrochemistry communications, Vol. 33, agost 2013, p. 84-87, ISSN 1388-2481 |
DOI: 10.1016/j.elecom.2013.04.023
El registro aparece en las colecciones:
Documentos de investigación >
Documentos de los grupos de investigación de la UAB >
Centros y grupos de investigación (producción científica) >
Ciencias >
Grupo de nanoingeniería de materiales, nanomagnetismo y nanomecánica (Gnm3)Artículos >
Artículos de investigaciónArtículos >
Artículos publicados
Registro creado el 2013-11-21, última modificación el 2023-03-08