Reduced hysteresis and enhanced air stability of low-temperature processed carbon-based perovskite solar cells by surface modification
Aung, Soe Ko Ko (Uppsala University. Department of Chemistry)
Vijayan, Anuja (Uppsala University. Department of Chemistry)
Karimipour, Masoud (Institut Català de Nanociència i Nanotecnologia)
Seetawan, Tosawat (Sakon Nakhon Rajabhat University)
Boschloo, Gerrit (Uppsala University. Department of Chemistry)

Fecha:	2023
Resumen:	Low temperature processed carbon-based perovskite solar cells (C-PSCs) have gained great interest because of low cost and ease of fabrication. By replacing the Au electrode with carbon, stable solar cells suited for mass-production process can be made. However, power conversion efficiencies (PCEs) of C-PSCs still lag behind that of PSCs with Au contact. Here we explore low temperature (≤150 °C) processed C-PSCs with, where a two-step method is used to prepare mixed-ion lead perovskite films, with tin oxide (SnO) electron transport layer, poly(3-hexylthiophene-2,5-diyl) (P3HT) hole transport layer and carbon electrode, resulting in devices with a PCE of 14. 0%. Moreover, hexyl trimethylammonium bromide (HTAB) was introduced to improve the interface between perovskite and P3HT. Perovskite grains were remarkably enlarged into micrometer-size and defects were reduced. As a result, a champion PCE of 16. 1% was obtained, mainly due to enhanced fill factor from 0. 67 to 0. 73. The interface modification by HTAB molecule is an effective way to passivate the perovskite defects and facilitate the carrier transport at the perovskite/HTL interface. Unencapsulated devices showed excellent stability over 1500 h stored under ambient air (relative humidity ∼ 50 ± 10%).
Derechos:	Aquest document està subjecte a una llicència d'ús Creative Commons. Es permet la reproducció total o parcial, la distribució, i la comunicació pública de l'obra, sempre que no sigui amb finalitats comercials, i sempre que es reconegui l'autoria de l'obra original. No es permet la creació d'obres derivades.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió publicada
Publicado en:	Electrochimica Acta, Vol. 443 (March 2023) , art. 141935, ISSN 0013-4686

DOI: 10.1016/j.electacta.2023.141935

10 p, 8.4 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados