Large exchange bias and its connection to interface structure in FeF2-Fe bilayers
Nogués, Josep (University of California-San Diego. Physics Department)
Lederman, D. (University of California, San Diego. Department of Physics)
Moran, T. J.. (University of California, San Diego. Department of Physics)
Schuller, Ivan K. (University of California, San Diego. Department of Physics)
Rao, K. V. (Kungl. Tekniska högskolan. Department of Condensed Matter Physics)
American Physical Society

Fecha:	1996
Resumen:	Large exchange bias effects (ΔE 1. 1 erg/cm2) were observed in antiferromagnetic (FeF2)-ferromagnetic (Fe) bilayers grown on MgO. The FeF2 grows along the spin-compensated (110) direction. The FeF2-Fe interface roughness was characterized using specular and diffuse x-ray diffraction and atomic force microscopy. The magnitude of the exchange bias field H E increases as the interface roughness decreases. These results imply that magnetic domain creation in the antiferromagnet plays an important role.
Nota:	This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics.
Derechos:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió publicada
Materia:	Exchange interactions ; Antiferromagnetism ; Interface roughness ; Atomic force microscopy ; Interface structure ; Magnetic domains
Publicado en:	Applied physics letters, Vol. 68, Issue 22 (May 1996) , p. 3186-3188, ISSN 1077-3118

DOI: 10.1063/1.115819

4 p, 346.4 KB