Home > Articles > Published articles > Electrochemical deposition of NiMnGa alloys |
Date: | 2016 |
Abstract: | An electrochemical synthesis route for NiMnGa alloys is presented. Thin films (TFs) of NiMnGa were fabricated by single step electrodeposition from aqueous electrolytes using direct current (DC) over a range of current densities. By meticulous electrolyte tuning, homogeneous TFs with high Ga and Mn content could be achieved at current densities as high as -400 mA cm-2. Detailed compositional analysis of the alloys showed that growth was homogeneous and oxygen content was minimized. TFs plated at very low current densities were found to be nanocrystalline/ amorphous. In order to obtain fully crystalline samples, thermal annealing was carried out. Mechanical characterization was assessed by nanoindentation, and the effect of Ga content on mechanical properties was investigated. |
Grants: | European Commission 336456 Ministerio de Economía y Competitividad RYC-2012-10839 Agència de Gestió d'Ajuts Universitaris i de Recerca 2014/SGR-1015 |
Note: | L'article final d'aquest post-print canvia pacialment el títol a: "Single step electrosynthesis of NiMnGa alloys" |
Rights: | Tots els drets reservats. |
Language: | Anglès |
Document: | Article ; recerca ; Versió acceptada per publicar |
Subject: | NiMnGa ; Single step electrodeposition ; Aqueous electrolyte ; Thin films |
Published in: | Electrochimica acta, Vol. 204 (June 2016) , p. 199-205, ISSN 1873-3859 |