Home > Articles > Published articles > Water affinity and surface charging at the z-Cut and y-Cut LiNbO3 surfaces : |
Date: | 2016 |
Abstract: | Polarization dependence of water adsorption and desorption on LiNbO₃ surfaces was demonstrated using X-ray photoelectron spectroscopy (XPS) carried out in situ under near-ambient conditions. Positive and negative (0001) faces (z-cut) of the same crystal were compared for the same temperature and pressure conditions. Our results indicate a preferential adsorption on the positive face of the crystal with increasing water pressure and also higher desorption temperature of the adsorbed molecular water at the positive face. Adsorption measurements on the (1100) face (y-cut) showed also strong affinity to water, as observed for the z-cut positive surface. We found a direct relation between the capacity of the surface to discharge and/or to screen surface charges and the affinity for water of each face. XPS spectra indicate the presence of OH groups at the surface for all the conditions and surfaces measured. |
Grants: | European Commission 308023 Ministerio de Economía y Competitividad FIS2015-73932-JIN Ministerio de Economía y Competitividad FIS2013-48668-C2-1-P Ministerio de Economía y Competitividad MAT2012-38319-C02-01 Agència de Gestió d'Ajuts Universitaris i de Recerca 2014/SGR-1216 |
Rights: | Tots els drets reservats. |
Language: | Anglès |
Document: | Article ; recerca ; Versió acceptada per publicar |
Subject: | Adsorption measurement ; Ambient conditions ; Ambient-pressure x-ray photoelectron spectroscopies ; Desorption temperatures ; Polarization dependence ; Preferential adsorption ; Surface charging ; Temperature and pressures |
Published in: | Journal of physical chemistry. C, Vol. 120, issue 42 (Oct. 2016) , p. 24048-24055, ISSN 1932-7455 |
Postprint 9 p, 430.7 KB |