Orientationally ordered silicon nanocrystal cuboctahedra in superlattices
Yu, Yixuan (University of Texas. Texas Materials Institute)
Lu, Xiaotang (University of Texas. Texas Materials Institute)
Guillaussier, Adrien (University of Texas. Texas Materials Institute)
Voggu, Vikas Reddy (University of Texas. Texas Materials Institute)
Pineros, William (University of Texas. Texas Materials Institute)
De La Mata, Maria (Institut Català de Nanociència i Nanotecnologia)
Arbiol i Cobos, Jordi (Institut Català de Nanociència i Nanotecnologia)
Smilgies, Detlef-M. (Cornell University. Cornell High Energy Synchrotron Source)
Truskett, Thomas M. (University of Texas. Texas Materials Institute)
Korgel, Brian A. (University of Texas. Texas Materials Institute)

Fecha: 2016
Resumen: Uniform silicon nanocrystals were synthesized with cuboctahedral shape and passivated with 1-dodecene capping ligands. Transmission electron microscopy, electron diffraction, and grazing incidence wide-angle and small-angle X-ray scattering show that these soft cuboctahedra assemble into face-centered cubic superlattices with orientational order. The preferred nanocrystal orientation was found to depend on the orientation of the superlattices on the substrate, indicating that the interactions with the substrate and assembly kinetics can influence the orientation of faceted nanocrystals in superlattices.
Nota: Número d'acord de subvenció MINECO/MAT2014-59961-C2-2-R
Nota: Número d'acord de subvenció MINECO/SEV-2013-0295
Nota: Número d'acord de subvenció AGAUR/2014/SGR-1638
Nota: This is an open access article published under an ACS AuthorChoice License. See Standard ACS AuthorChoice/Editors’ Choice Usage Agreement - https://pubs.acs.org/page/policy/authorchoice_termsofuse.html
Derechos: Tots els drets reservats.
Lengua: Anglès.
Documento: article ; recerca ; acceptedVersion
Publicado en: Nano Letters, Vol. 16, issue 12 (2016) , p. 7814-7821, ISSN 1530-6992

DOI: 10.1021/acs.nanolett.6b04006


8 p, 9.7 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados

 Registro creado el 2019-01-14, última modificación el 2019-03-28



   Favorit i Compartir