Hierarchical Porous Ni3S4 with Enriched High-Valence Ni Sites as a Robust Electrocatalyst for Efficient Oxygen Evolution Reaction
Wan, Kai (Katholieke Universiteit Leuven. Department of Materials Engineering)
Luo, Jiangshui (Katholieke Universiteit Leuven. Department of Materials Engineering)
Zhou, Chen (Katholieke Universiteit Leuven. Department of Materials Engineering)
Zhang, Ting (Institut Català de Nanociència i Nanotecnologia)
Arbiol i Cobos, Jordi (Institut Català de Nanociència i Nanotecnologia)
Lu, Xihong (Sun Yat-Sen University)
Mao, Bing-Wei (Xiamen University)
Zhang, Xuan (Katholieke Universiteit Leuven. Department of Materials Engineering)
Fransaer, Jan (Katholieke Universiteit Leuven. Department of Materials Engineering)

Fecha: 2019
Resumen: Electrochemical water splitting is a common way to produce hydrogen gas, but the sluggish kinetics of the oxygen evolution reaction (OER) significantly limits the overall energy conversion efficiency of water splitting. In this work, a highly active and stable, meso-macro hierarchical porous Ni S architecture, enriched in Ni is designed as an advanced electrocatalyst for OER. The obtained Ni S architectures exhibit a relatively low overpotential of 257 mV at 10 mA cm and 300 mV at 50 mA cm . Additionally, this Ni S catalyst has excellent long-term stability (no degradation after 300 h at 50 mA cm ). The outstanding OER performance is due to the high concentration of Ni and the meso-macro hierarchical porous structure. The presence of Ni enhances the chemisorption of OH , which facilitates electron transfer to the surface during OER. The hierarchical porosity increases the number of exposed active sites, and facilitates mass transport. A water-splitting electrolyzer using the prepared Ni S as the anode catalyst and Pt/C as the cathode catalyst achieves a low cell voltage of 1. 51 V at 10 mA cm . Therefore, this work provides a new strategy for the rational design of highly active OER electrocatalysts with high valence Ni and hierarchical porous architectures.
Nota: Número d'acord de subvenció AGAUR/2017/SGR-327
Nota: Número d'acord de subvenció MINECO/ENE2017-85087-C3
Nota: Número d'acord de subvenció MINECO/SEV-2013-0295
Derechos: Tots els drets reservats.
Lengua: Anglès.
Documento: article ; recerca ; submittedVersion
Materia: Durability ; Hierarchical porous structure ; High-valence Ni3+ ; Ni3S4 ; Oxygen evolution reaction
Publicado en: Advanced functional materials, Vol. 29, Issue 18 (May 2019) , art. 1900315, ISSN 1616-3028

DOI: 10.1002/adfm.201900315


Preprint
42 p, 2.9 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados

 Registro creado el 2020-02-06, última modificación el 2020-05-07



   Favorit i Compartir