Synthesis and Caracterization of Mesoporous FePO4 as Positive Electrode Materials for Lithium Batteries
Salamani, Amel (Université Mohamed Boudiaf-M'sila)
Merrouche, Abdallah (Université Mohamed Boudiaf-M'sila)
Telli, Laid (Université Mohamed Boudiaf-M'sila)
Gómez-Romero, Pedro 1959- (Institut Català de Nanociència i Nanotecnologia)
Cabán Huertas, Zahilia (Institut Català de Nanociència i Nanotecnologia)

Fecha:	2018
Resumen:	Mesoporous iron phosphates were synthesized using sodium dodecyl sulfate (SDS) and cetyltrimethylammonium bromide (CTAB) as surfactants. The material synthesized in the presence of SDS was not applied as a positive electrode active material of a lithium battery. The results show that the obtained FePO has a mesoporous structure with a specific surface area of 70 m g and a dominant pore diameter of 3 nm. Those mesoporous were characterized by different microstructural and electrochemical analyzes. Among the materials studied under different conditions, those calcined at 450°C preserve mesoporous structures and exhibit the best electrochemical performance when used as active materials of the positive electrodes of lithium batteries. Effectively, a relatively high specific capacity of 135 and 122 mAh g was registered at C/20 collected experimentally by the samples synthesized in the presence of SDS and CTAB, respectively.
Derechos:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió acceptada per publicar
Materia:	Lithium batteries ; Positive electrodes ; Mesoporous materials ; Iron phosphate ; Electrochemical tests
Publicado en:	Surface engineering and applied electrochemistry, Vol. 54, Issue 1 (January 2018) , p. 55-63, ISSN 1934-8002

DOI: 10.3103/S106837551801012X

Postprint 16 p, 595.0 KB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados