Melt synthesis and characterization of synthetic Mn-rich tainiolite
Baumgartner, Alexander (University of Bayreuth. Department of Inorganic Chemistry I)
Butterhof, Christian (University of Bayreuth. Department of Inorganic Chemistry I)
Koch, Sebastian (University of Bayreuth. Department of Inorganic Chemistry I)
Mariychuk, Ruslan (University of Bayreuth. Department of Inorganic Chemistry I)
Breu, Josef (University of Bayreuth. Department of Inorganic Chemistry I)

Fecha:	2009
Resumen:	Large transition-metal contents add desirable physical properties, such as redox reactivity, magnetism, and electric or ionic conductivity to micas and make them interesting for a variety of materials-science applications. A Mn- and F-rich tainiolite mica, Cs(Mn Li)SiOF, was synthesized by a high-temperature melt-synthesis technique. Subsequent annealing for 10 days led to a single-phase and coarse-grained material. Single-crystal X-ray diffraction studies were performed and characteristic geometric parameters were compared to the analogous ferrous compound, synthetic Fe-rich tainiolite, Cs(Fe Li)SiOF. Both tainiolite structures are outside the compositional stability limits for the 2:1 layer structure, and incorporating the relatively large cation Mn requires significant structural adjustments in both the octahedral and tetrahedral sheets. As expected, increasing the ionic radius of the octahedral cation from0. 78 Å (Fe) to 0. 83 Å (Mn) reduces the octahedral flattening angle from <ψ> = 57. 05° to <ψ> = 56. 4°, the smallest value ever observed for a tetrasilicic mica. However, even this small <ψ> value is insufficient to match the lateral sizes of the tetrahedral and octahedral sheets and, in addition, unusual structural adjustments in the tetrahedral sheet are required. The average tetrahedral bond length <T-O> is much greater (1. 643 Å) than the average value observed for tetrasilicic micas (1. 607 Å,) and a significant difference between the <T-O> (1. 605 Å) and the <T-O> bond lengths (1. 656 Å) and an enlarged basal flattening angle (τ = 106. 29°) are noted. These parameters indicate: (1) that the 2:1 layer might be more flexible than previously thought, to allow matching of the lateral dimensions of the tetrahedral and octahedral sheets; and (2) that many other compositions that appear interesting from a materials-science point of view might be accessible.
Derechos:	Tots els drets reservats.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió publicada
Materia:	Crystal Chemistry ; Manganese ; Mica ; Synthetic Clays ; Tainiolite
Publicado en:	Clays and Clay Minerals, Vol. 57, Núm. 2 (2009) , p. 271-277, ISSN 1552-8367

DOI: 10.1346/CCMN.2009.0570213