Identification of neoformed Ni-phyllosilicated upon Ni uptake in montmorillonite : A transmission electron microscopy and extended x-ray absorption fine structure study
Dähn, Rainer (Paul Scherrer Institut. Laboratory for Waste Management)
Jullien, Michel (Commissariat à l'Énergie Atomique et aux Énergies Alternatives (França))
Scheidegger, Andrè M. (Paul Scherrer Institut. Laboratory for Waste Management)
Poinssot, Christophe (Commissariat à l'Énergie Atomique et aux Énergies Alternatives (França))
Baeyens, Bart (Paul Scherrer Institut. Laboratory for Waste Management)
Bradbury, Michael H. (Paul Scherrer Institut. Laboratory for Waste Management)

Fecha:	2006
Resumen:	The aim of this work was to investigate whether neoformed Ni-phyllosilicates can be observed and identified using transmission electron microscopy (TEM) in combination with energy dispersive spectroscopy (EDS). The investigations focused on Ni-phyllosilicates formed from Ni-doped montmorillonite. The reaction conditions (pH 8, [Ni] = 660 and 3300 μM, 0. 2 M Ca(NO)) employed were similar to those used in previous polarized extended X-ray absorption fine structure (PEXAFS) investigations of neoformed Ni-phyllosilicates in a Ni-montmorillonite system. The TEM investigations of Ni-doped montmorillonite revealed the presence of small, thin particles consisting of coherent stacks that yielded only three to five lattice fringes with spacings consistent with smectites. These small particles were neoformed phyllosilicates, based on the fact that the small particles were only observed in Ni-doped samples and their Ni content, as determined from EDS analysis, was high (up to 10 wt. % NiO). Furthermore, the particles did not possess the characteristic properties of montmorillonite particles, such as a 2:1 Si to Al ratio; instead these particles were rich in Si (up to 75 wt. % SiO). Unlike montmorillonite, these particles did not contain any Fe. The particles were also significantly more resistant to electron beam damage than montmorillonite particles, and EXAFS measurements confirmed the presence of neoformed Ni-phyllosilicates. The TEM study further indicates the presence of a variety of additional minerals (e. g. cristobalite, halloysite) and an X-ray amorphous Si-rich phase. A Ni signal could only be detected in the latter phase at high Ni loadings (403 μmol/g), suggesting that Ni uptake at low metal loadings (<90 μmol/g) is mainly controlled by the neoformation of phyllosilicates.
Derechos:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió publicada
Materia:	EXAFS ; Montmorillonite ; Neoformed Phyllosilicates ; Ni ; TEM
Publicado en:	Clays and Clay Minerals, Vol. 54, Núm. 2 (2006) , p. 209-219, ISSN 1552-8367

DOI: 10.1346/CCMN.2006.0540206

11 p, 1.1 MB  Acceso restringido a la UAB

El registro aparece en las colecciones:
Artículos > Artículos de investigación
Artículos > Artículos publicados