Nanosecond Laser-Assisted Nitrogen Doping of Graphene Oxide Dispersions
Kepić, Dejan (Institut de Ciència de Materials de Barcelona)
Sandoval, Stefania (Institut de Ciència de Materials de Barcelona)
Pérez del Pino, Ángel (Institut de Ciència de Materials de Barcelona)
Gyorgy, Eniko (Institut de Ciència de Materials de Barcelona)
Cabana Jiménez, Laura (Institut de Ciència de Materials de Barcelona)
Ballesteros, Belén (Institut Català de Nanociència i Nanotecnologia)
Tobias, Gerard (Institut de Ciència de Materials de Barcelona)

Fecha:	2017
Resumen:	N-doped reduced graphene oxide (RGO) has been prepared in bulk form by laser irradiation of graphene oxide (GO) dispersed in an aqueous solution of ammonia. A pulsed Nd:YAG laser with emission wavelengths in the infrared (IR) 1064 nm, visible (Vis) 532 nm, and ultraviolet (UV) 266 nm spectral regions was employed for the preparation of the N-doped RGO samples. Regardless of the laser energy employed, the resulting material presents a higher fraction of pyrrolic nitrogen compared to nitrogen atoms in pyridinic and graphitic coordination. Noticeably, whereas increasing the laser fluence of UV and Vis wavelengths results in an increase in the total amount of nitrogen, up to 4. 9 at. % (UV wavelength at 60 mJ cm fluence), the opposite trend is observed when the GO is irradiated in ammonia solution through IR processing. The proposed laser-based methodology allows the bulk synthesis of N-doped reduced graphene oxide in a simple, fast, and cost efficient manner.
Ayudas:	Ministerio de Economía y Competitividad SEV-2013-0295 Ministerio de Economía y Competitividad SEV-2015-0496 Ministerio de Economía y Competitividad MAT2014-53500-R Ministerio de Economía y Competitividad ENE2014-56109-C3-3-R
Derechos:	Tots els drets reservats.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió acceptada per publicar
Materia:	Ammonia ; Graphene ; Lasers ; N-doping ; Reduced graphene oxide
Publicado en:	ChemPhysChem, Vol. 18, Issue 8 (April 2017) , p. 935-941, ISSN 1439-7641

DOI: 10.1002/cphc.201601256

Postprint 12 p, 402.9 KB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados