Mesoporous titania powders: the role of precursors, ligand addition and calcination rate on their morphology, crystalline structure and photocatalytic activity
Masolo, Elisabetta (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)
Meloni, Manuela (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)
Garroni, Sebastiano (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)
Mulas, Gabriele (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)
Enzo, Stefano (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)
Baró, M. D.. (Universitat Autònoma de Barcelona. Departament de Física)
Rossinyol Casals, Emma (Universitat Autònoma de Barcelona. Servei de Microscòpia)
Rzeszutek, Agnieszka (Helmholtz-Zentrum Geesthacht. Das Institut für Werkstoffforschung)
Herrmann-Geppert, Iris (Helmholtz-Zentrum Geesthacht. Das Institut für Werkstoffforschung)
Maria Pilo, Maria (Università degli Studi di Sassari. Dipartimento di Chimica e Farmacia)

Fecha:	2014
Resumen:	We evaluate the influence of the use of different titania precursors, calcination rate, and ligand addition on the morphology, texture and phase content of synthesized mesoporous titania samples, parameters which, in turn, can play a key role in titania photocatalytic performances. The powders, obtained through the evaporation-induced self-assembly method, are characterized by means of ex situ X-Ray Powder Diffraction (XRPD) measurements, N2 physisorption isotherms and transmission electron microscopy. The precursors are selected basing on two different approaches: the acid-base pair, using TiCl4 and Ti(OBu)4, and a more classic route with Ti(OiPr)4 and HCl. For both precursors, different specimens were prepared by resorting to different calcination rates and with and without the addition of acetylacetone, that creates coordinated species with lower hydrolysis rates, and with different calcination rates. Each sample was employed as photoanode and tested in the water splitting reaction by recording I-V curves and comparing the results with commercial P25 powders. The complex data framework suggests that a narrow pore size distribution, due to the use of acetylacetone, plays a major role in the photoactivity, leading to a current density value higher than that of P25.
Ayudas:	Ministerio de Economía y Competitividad MAT2010-20616-C02-02 Agència de Gestió d'Ajuts Universitaris i de Recerca 2009/SGR-1292
Derechos:	Aquest document està subjecte a una llicència d'ús Creative Commons. Es permet la reproducció total o parcial, la distribució, la comunicació pública de l'obra i la creació d'obres derivades, fins i tot amb finalitats comercials, sempre i quan es reconegui l'autoria de l'obra original.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió publicada
Materia:	Titania ; Titani ; EISA method ; Evaporation-induced self-assembly method ; Mètode EISA ; Powders ; Pols ; Photocatalysis ; Fotocatàlisi ; Water splitting ; Dissociació de l'aigua
Publicado en:	Nanomaterials, Vol. 4, no. 3 (2014) , p. 583-598, ISSN 2079-4991

DOI: 10.3390/nano4030583
PMID: 28344237

16 p, 3.3 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Grupo de nanoingeniería de materiales, nanomagnetismo y nanomecánica (Gnm3)
Artículos > Artículos de investigación
Artículos > Artículos publicados