Micelle-assisted electrodeposition of highly mesoporous Fe-Pt nodular films with soft magnetic and electrocatalytic properties
Isarain-Chávez, E. (Universitat Autònoma de Barcelona. Departament de Física)
Baró, M. D. (Universitat Autònoma de Barcelona. Departament de Física)
Pellicer Vilà, Eva M. (Eva Maria) (Universitat Autònoma de Barcelona. Departament de Física)
Sort Viñas, Jordi (Universitat Autònoma de Barcelona. Departament de Física)

Data: 2017
Resum: Mesoporous Fe–Pt nodular films (with a regular spatial arrangement of sub-15 nm pores) are grown onto evaporated Au, Cu and Al conductive layers by micelle-assisted electrodeposition from metal chloride salts in the presence of Pluronic P123 tri-block copolymer dissolved in the aqueous electrolytic bath. This synthetic approach constitutes a simple, one-step, versatile procedure to grow multifunctional mesoporous layers appealing for diverse applications that take advantage of materials with an ultra-high surface area-to-volume ratio. The films exhibit tuneable composition with relative Fe/Pt weight ratios, disregarding oxygen, varying from 4/96 to 52/48. All the mesoporous alloys show a soft magnetic behaviour with tuneable saturation magnetization and coercivity values (the latter ranging from ca. 5 Oe to 40 Oe). In addition, the Au/Fe–Pt deposits (even the ones with higher Fe content) exhibit good performance towards hydrogen evolution reaction in both alkaline and acidic media due to the inherent mesoporosity, with excellent stability after running 50 cycles. The interest of alloying Fe with Pt is thus two-fold: (i) to confer magnetic properties to the mesoporous alloys and (ii) to reduce the amount of the costly noble metal in the electrocatalyst in an environmentally sustainable manner.
Nota: Número d'acord de subvenció EC/H2020/648454
Nota: Número d'acord de subvenció MINECO/MAT2017-86357-C3-1-R
Nota: Número d'acord de subvenció MINECO/MAT2014-57960-C3-1-R
Nota: Número d'acord de subvenció MINECO/RYC-2012-10839
Nota: Número d'acord de subvenció AGAUR/2014/SGR-1015
Drets: Tots els drets reservats
Llengua: Anglès.
Document: article ; recerca ; acceptedVersion
Publicat a: Nanoscale, Vol. 9, issue 45 (Dec. 2017) , art. 18081, ISSN 2040-3364

DOI: 10.1039/C7NR05561G


Post-print
16 p, 2.9 MB

El registre apareix a les col·leccions:
Documents de recerca > Documents dels grups de recerca de la UAB > Centres i grups de recerca (producció científica) > Ciències > Grup de nanoenginyeria de materials, nanomagnetisme i nanomecànica (Gnm3) > SPIN-PORICS
Articles > Articles de recerca
Articles > Articles publicats

 Registre creat el 2018-04-19, darrera modificació el 2019-02-18



   Favorit i Compartir