Characterization of NiO-Al2O3 composite and its conductivity in biogas for solid oxide fuel cell
Patil, Sarika P. (Shivaji University. Department of Physics)
Jadhav, L. D. (Rajaram College. Department of Physics)
Dubal, Deepak P. (Institut Català de Nanociència i Nanotecnologia)
Puri, V. R. (Shivaji University. Department of Physics)

Data:	2016
Resum:	NiO-Al O nanocomposite has been synthesized by mixing combustion synthesized powders. The nanocomposite is an effective anode/anode functional layer for intermediate temperature solid oxide fuel cells. The TEM of NiO and Al O revealed spherical particles of 30 nm and platelets of 70 nm, respectively. The XRD analysis of NiO-Al O composite sintered at 900 °C showed presence of cubic NiO and rhombohedral α-Al O which were chemically stable. However, above 1200 °C NiAl O started to appear. The conductivity of NiO-Al O was the highest in hydrogen (4. 3 × 10 S/cm at 600 °C). In biogas, the conductivity was 3. 2 × 10 S/cm with the activation energy of 0. 67 eV. The stability of the composite in biogas was also examined.
Drets:	Aquest document està subjecte a una llicència d'ús Creative Commons. Es permet la reproducció total o parcial, la distribució, i la comunicació pública de l'obra, sempre que no sigui amb finalitats comercials, i sempre que es reconegui l'autoria de l'obra original. No es permet la creació d'obres derivades.
Llengua:	Anglès
Document:	Article ; recerca ; Versió publicada
Matèria:	Oxides ; Chemical synthesis ; X-ray diffraction ; Electrical conductivity ; Microstructure
Publicat a:	Materials Science- Poland, Vol. 34, Issue 2 (June 2016) , p. 266-274, ISSN 2083-134X

DOI: 10.1515/msp-2016-0045

9 p, 1.2 MB

El registre apareix a les col·leccions:
Documents de recerca > Documents dels grups de recerca de la UAB > Centres i grups de recerca (producció científica) > Ciències > Institut Català de Nanociència i Nanotecnologia (ICN2)
Articles > Articles de recerca
Articles > Articles publicats