Electrochemically synthesized mesoporous thin films of ZnO for highly efficient dye sensitized solar cells
Lima, F. Anderson S. (Institut Català de Nanociència i Nanotecnologia)
Vasconcelos, Igor F. (Universidade Federal do Ceará. Departamento de Engenharia Metalúrgica e de Materiais)
Lira-Cantu, Monica (Institut Català de Nanociència i Nanotecnologia)

Fecha:	2015
Resumen:	Abstract In this work, nanostructured thin films of ZnO were electrochemically grown on FTO substrates. The morphology was tuned by modifying the synthesis parameters. The synthesis was carried out by applying Zn(NO<inf>3</inf>)·6H<inf>2</inf>O as the sole component of the aqueous electrolyte, avoiding the use of capping agents. The composition and morphology of the prepared ZnO were characterized by energy-dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM), respectively. The as-deposited films were applied as electrodes in dye sensitized solar cells (DSCs). The performance of the cells was investigated by J×V curves and IPCE (incident photon to charge carrier efficiency) measurements. The SEM analysis demonstrated a direct relationship between ZnO morphology and Zn precursor concentration. It has been shown that the lower the concentration is, the more porous the morphology is. Increasing the amount of dye adsorbed on the ZnO decreased the power conversion efficiency of the final DSCs. The best cell presented the following parameters: open circuit voltage <sup>VOC</sup>=0. 59V, short circuit current <sup>JSC</sup>=7. 64mA/<sup>cm2</sup>, fill factor FF=50. 41%, and power conversion efficiency PCE=2. 27%.
Derechos:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió sotmesa a revisió
Materia:	Dye sensitized solar cells ; Electrodeposition ; ZnO
Publicado en:	Ceramics international, Vol. 41, Issue 8 (September 2015) , p. 9314-9320, ISSN 0272-8842

DOI: 10.1016/j.ceramint.2015.03.271

Preprint 10 p, 1.0 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados