Optimizing the mechanical strength of adobe bricks
Schicker, A. (University of Vienna. Department of Geodynamics and Sedimentology)
Gier, Susanne (University of Vienna. Department of Geodynamics and Sedimentology)

Date:	2009
Abstract:	Ecologic building materials such as adobe bricks have become of greater economic importance in recent years. In the present work, the addition of selected materials to improve the compressive and bending strengths of adobe bricks was tested. The raw material (loam UD) was analyzed for its mineralogical and chemical composition. The loam studied consisted of quartz, feldspar, and the clay minerals chlorite, vermiculite, illite, and kaolinite. Prerequisites for using this loam for brick making were its grain-size distribution and the absence of expandable clayminerals. To optimize the compressive and bending strengths of the adobe bricks, seven natural and 'eco-friendly' synthetic additives were admixed with the raw material and homogenized. From this material, small adobe bricks and bars were made. One series of bricks and bars was made without additives but instead was coated with a hydrophobic impregnation cream. The bricks were stored for up to 20 days at 100 and 75% relative humidity (RH). After 1, 5, and 20 days, the compressive and bending strengths were measured to identifythe critical humiditylevel for brick strength. The compressive and bending strengths of loam UD at dryconditions without additives showed values of 9 N/mm and 4. 8 N/mm, respectively. With some of the additives, the strength improved by up to 30%. The greatest increases in strength were achieved bymixing the loam with Acronal S650. Finelyground trass and diatomite also increased the drystrength. After storage at high levels of RH, these mixtures lost >50% strength. In contrast, the loam mixed with blast-furnace slag has a small initial strength but showed the smallest decreases in strength after exposure to high levels of RH.
Rights:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Language:	Anglès
Document:	Article ; recerca ; Versió publicada
Subject:	Adobe Bricks ; Bending Strength ; Compressive Strength ; Industrial Application of Clay ; Load Capacity
Published in:	Clays and Clay Minerals, Vol. 57, Núm. 4 (2009) , p. 494-501, ISSN 1552-8367

DOI: 10.1346/CCMN.2009.0570410