Some physicochemical properties of the white sepiolite known as pipestone from Eski̇şehi̇r, Turkey
Önal, Müserref (Ankara University. Department of Chemistry)
Yilmaz, Hamza (Ankara University. Department of Chemistry)
Sarikaya, Yüksel (Ankara University. Department of Chemistry)

Data: 2008
Resum: Various physicochemical characteristics of a sepiolite sample from the Eskişehir area, Turkey, were investigated to help in making predictions about possible uses of the material. The sample was examined by chemical analysis (CA), thermal analysis (DTA/TGA), X-ray diffraction (XRD) analysis, particle-size analysis (PSA), linear dilatometry (LD), scanning electron microscopy (SEM), mercury porosimetry (Hg-Por. ), and low-temperature nitrogen adsorption/desorption (N-AD) techniques. The CA and XRD data indicated that the sepiolite contains only 6% dolomite by mass. The XRD patterns showed that sepiolite anhydride, enstatite, diopside, and opal-CT form upon heating the sepiolite above 600, 800, 900, and 1200°C, respectively. The maximum rate of endothermic changes in the DTA and TGA curves were observed at 82, 287, and 491°C, corresponding to the loss of external, zeolitic, and bound water from the sepiolite, respectively. Dehydroxylation and recrystallization of the sepiolite were fastest at 845°C and 862°C, respectively. The LD curve indicated that the shrinkage began at 800°C and reached 4. 0% at 1000°C. The proportion of particles with diameters of <2 μm, and the external surface area of the long-term (24 h) water-treated sepiolite were determined by PSA as 79% by volume, and 8 mg, respectively. The SEM view revealed discrete bundles of sepiolite fibers of various lengths. The specific surface area found from adsorption data was 316 mg. The specific micro-, meso-, macro-, and total-pore volumes obtained from the combination of Hg-Por. and N-AD results were 0. 16, 0. 21, 0. 45, and 0. 82 cmg, respectively. The average macropore and micro-mesopore radii in the sepiolite were estimated (using the Hg-Por. and N-AD data) tobe 35 and 2. 4 nm, respectively.
Drets: Tots els drets reservats.
Llengua: Anglès
Document: article ; recerca ; publishedVersion
Matèria: Porosity ; Sepiolite ; Surface area ; Thermal analysis ; X-ray diffraction
Publicat a: Clays and Clay Minerals, Vol. 56, Núm. 5 (2008) , p. 511-519, ISSN 1552-8367

DOI: 10.1346/CCMN.2008.0560504


9 p, 839.9 KB
 Accés restringit a la UAB

El registre apareix a les col·leccions:
Articles > Articles de recerca
Articles > Articles publicats

 Registre creat el 2020-06-10, darrera modificació el 2020-10-09



   Favorit i Compartir