Pàgina inicial > Articles > Articles publicats > Electrodeposition of sizeable and compositionally tunable rhodium-iron nanoparticles and their activity toward hydrogen evolution reaction |
Data: | 2016 |
Resum: | Rh-Fe nanoparticles (NPs) with variable Rh/Fe ratios have been obtained by direct current electrodeposition onto Au-metalized Si/Ti substrates from an electrolyte containing Rh(III) and Fe(III) chloride salts. NP mean diameter could be varied in the range of 20-80 nm by playing with the applied current density (-j = 0. 5-2 mA cm-2) and deposition times (t = 200-3200 s). NPs were very well adhered to the substrate and became progressively enriched in Fe as the absolute value of the current density increased. X-ray photoelectron spectroscopy analyses revealed that the NPs are mostly metallic. The oxygen signal detected at surface level is relatively high but reduces down to less than 1 at% after 1 min Ar ions sputtering. The as-deposited Rh-Fe NPs are active toward hydrogen evolution reaction in alkaline medium. Different values of the onset potential for water reduction have been observed depending on the j and t values applied for NPs growth. Cycling stability tests reveal that NPs do not suffer from excessive deterioration of their electrocatalytic activity with time. |
Ajuts: | European Commission 648454 European Commission 336456 Ministerio de Economía y Competitividad MAT2014-57960-C3-1-R Ministerio de Economía y Competitividad RYC-2012-10839 Agència de Gestió d'Ajuts Universitaris i de Recerca 2014/SGR-1015 |
Drets: | Aquest document està subjecte a una llicència d'ús Creative Commons. Es permet la reproducció total o parcial, la distribució, i la comunicació pública de l'obra, sempre que no sigui amb finalitats comercials, i sempre que es reconegui l'autoria de l'obra original. No es permet la creació d'obres derivades. |
Llengua: | Anglès |
Document: | Article ; recerca ; Versió acceptada per publicar |
Matèria: | Nanoparticles ; Electrodeposition ; Hydrogen evolution reaction ; Rhodium-iron |
Publicat a: | Electrochimica acta, Vol. 194 (Marzo 2016) , p. 263-275, ISSN 1873-3859 |
Post-print 28 p, 131.1 KB |