Selective CO₂ capture in metal-organic frameworks with azine-functionalized pores generated by mechanosynthesis
Masoomi, Mohammad Yaser (Tarbiat Modares University. Department of Chemistry)
Stylianou, Kyriakos C. (Institut Català de Nanociència i Nanotecnologia)
Morsali, Ali (Tarbiat Modares University. Department of Chemistry)
Retailleau, Pascal (Centre national de la recherche scientifique (França). Institut de Chimie des Substances Naturelles)
Maspoch Comamala, Daniel (Institut Català de Nanociència i Nanotecnologia)

Fecha:	2014
Resumen:	Two new three-dimensional porous Zn(II)-based metal-organic frameworks, containing azine-functionalized pores, have been readily and quickly isolated via mechanosynthesis, by using a nonlinear dicarboxylate and linear N-donor ligands. The use of nonfunctionalized and methyl-functionalized N-donor ligands has led to the formation of frameworks with different topologies and metal-ligand connectivities and therefore different pore sizes and accessible volumes. Despite this, both metal-organic frameworks (MOFs) possess comparable BET surface areas and CO₂ uptakes at 273 and 298 K at 1 bar. The network with narrow and interconnected pores in three dimensions shows greater affinity for CO compared to the network with one-dimensional and relatively large pores-attributable to the more effective interactions with the azine groups.
Ayudas:	European Commission 300390 Ministerio de Economía y Competitividad MAT2012-30994 Ministerio de Ciencia e Innovación CTQ2011-16009-E
Derechos:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Lengua:	Anglès
Documento:	Article ; recerca ; Versió acceptada per publicar
Materia:	Accessible volume ; Different pore sizes ; Effective interactions ; Interconnected pores ; Mechanosynthesis ; Metal organic framework ; Metalorganic frameworks (MOFs) ; Three dimensions
Publicado en:	Crystal Growth and Design, Vol. 14, issue 5 (May 2014) , p. 2092-2096, ISSN 1528-7505

DOI: 10.1021/cg500033b

Postprint 6 p, 1.1 MB

El registro aparece en las colecciones:
Documentos de investigación > Documentos de los grupos de investigación de la UAB > Centros y grupos de investigación (producción científica) > Ciencias > Institut Català de Nanociència i Nanotecnologia (ICN2)
Artículos > Artículos de investigación
Artículos > Artículos publicados