Tailoring the physical properties of electrodeposited CoNiReP alloys with large Re content by direct, pulse, and reverse pulse current techniques
Pané i Vidal, Salvador (Institute of Robotics and Intelligent Systems)
Suriñach, Santiago (Universitat Autònoma de Barcelona. Departament de Física)
Özkale, Berna (Institute of Robotics and Intelligent Systems)
Sivaraman, Kartik M. (Institute of Robotics and Intelligent Systems)
Ruiz-Camps, C. (Universitat Autònoma de Barcelona. Departament de Física)
Baró, M. D. (Universitat Autònoma de Barcelona. Departament de Física)
Nelson, Bradley J. (Institute of Robotics and Intelligent Systems)
Sort Viñas, Jordi (Universitat Autònoma de Barcelona. Departament de Física)
Pellicer Vilà, Eva Maria (Universitat Autònoma de Barcelona. Departament de Física)

Data:	2013
Resum:	The composition, surface morphology and structure of CoNiReP alloy films with large Re content (up to 27 at%), obtained in a citrate-glycine based electrolyte have been studied as a function of the electrodeposition technique. Direct current (DC), pulse plating (PP) and reverse pulse plating (RPP) were considered with cathodic current densities from -50 mA cm-2 to -250 mA cm-2. The mechanical and magnetic properties have been analyzed and the data obtained has been correlated with composition and crystallographic structure. For values of j (DC), jon (PP) and jc (RPP) below -100 mA cm-2, Co-rich, P-containing deposits are obtained. Beyond these current densities, both the quantities of Ni and Re increase simultaneously at the expense of Co and P, the latter virtually falling to zero. The highest Re percentage (25-27 at%) was achieved in both PP and RPP conditions at a cathodic pulse of -250 mA cm-2. All the films were either entirely nanocrystalline in nature or partially amorphous. Hardness values as high as 9. 2 GPa have been found in PP plated Co64Ni18Re18 deposits. Besides the large hardness, the incorporation of Re in the films leads to high elastic recovery values. The magnetic character of the deposits ranges from soft to semi-hard ferromagnetic.
Ajuts:	Ministerio de Economía y Competitividad MAT2011-27380-C02-01 Agència de Gestió d'Ajuts Universitaris i de Recerca 2009/SGR-1292
Nota:	This is the author's version of a work that was accepted for publication in Electrochimica acta. Changes resulting from the publishing process, such as peer review, editing, corrections, structural formatting, and other quality control mechanisms may not be reflected in this document. Changes may have been made to this work since it was submitted for publication. A definitive version was subsequently published in Electrochimica acta, [96,(2013)] DOI10.1016/j.electacta.2013.02.077)
Drets:	Aquest material està protegit per drets d'autor i/o drets afins. Podeu utilitzar aquest material en funció del que permet la legislació de drets d'autor i drets afins d'aplicació al vostre cas. Per a d'altres usos heu d'obtenir permís del(s) titular(s) de drets.
Llengua:	Anglès
Document:	Article ; recerca ; Versió acceptada per publicar
Matèria:	Galvanoplàstia ; Electroformació
Publicat a:	Electrochimica acta, Vol. 96, abril 2013, p. 43-50, ISSN 1873-3859

DOI: 10.1016/j.electacta.2013.02.077

Post-print 10 p, 1.4 MB

El registre apareix a les col·leccions:
Documents de recerca > Documents dels grups de recerca de la UAB > Centres i grups de recerca (producció científica) > Ciències > Grup de nanoenginyeria de materials, nanomagnetisme i nanomecànica (Gnm3)
Articles > Articles de recerca
Articles > Articles publicats